低合金高强钢无预热或低温预热激光-电弧复合热源焊接技术

发布日期:2012-02-29 文章作者:雷振 王旭友 滕彬 林尚扬 文章来源:机械制造文摘-焊接分册 浏览次数:4823次

摘要:介绍了低合金高强钢无预热或低温预热激光一电弧复合热源焊接艺,对比研究了激光- MAG复合热源及常规MAG两种焊接T艺方法焊接低合金高强钢的冷裂纹敏感性及接头的力学性能。

关键词:激光;MAG电弧;复合热源焊接;低合金高强钢;无预热

中图分类号:TG156

Laser-arc Hybrid Welding Technology for Low-alloy High Strength Steel

        with Low Temperature Preheating or without Preheating

 Lei Zhen, Wang Xuyou, Teng Bin, Lin Shangyang

( Harbin Welding Institute, Heilongjiang, Harbin 150080)

Abstract :  Laser-arc hybrid welding technology for low-alloy high strength steel with low temperature preheating or non-preheating

was introduced. Compared the welding process between laser-MAG hybrid welding and MAG welding, the cold crack-sensitivity and

mechanical properties of the low-alloy high strength steel welded joints were investigated.

Key words:  laser;  MAG arc;  hybrid welding ;  low-alloy high strength steel;  non-preheating

0前    言

   大多数高强钢均具有较高的淬硬倾向,常规弧焊等焊接方法在焊接高强钢时,焊接接头易产生冷裂纹,为防止焊接冷裂纹的产生,焊前需要对待焊件进行预热,预热温度的高低主要取决于高强钢的化学成分、强度等级、母材厚度以及焊接结构等。一般而言,母材的碳当量及强度等级越高、母材厚度越大,焊前的预热温度就越高。尽管焊前预热处理能改善焊接接头的冷裂纹敏感性,但是却存在一系列问题。一方面,焊前预热使得焊接艺变得复杂,降低了焊接效率;另一方面,某些经高温预热后的件恶化了T人的操作环境;再者,对于某些形状复杂或尺寸较大的件无法进行有效的预热处理,这样对焊接T作带来较大的困难。